司太力合金涂层的制备及与液态铅铋相容性研究

张天一 吕沙沙 阮章顺 付晓刚 龙斌 陶柳 秦博 李正操

张天一, 吕沙沙, 阮章顺, 付晓刚, 龙斌, 陶柳, 秦博, 李正操. 司太力合金涂层的制备及与液态铅铋相容性研究[J]. 材料开发与应用, 2023, 38(6): 9-14.
引用本文: 张天一, 吕沙沙, 阮章顺, 付晓刚, 龙斌, 陶柳, 秦博, 李正操. 司太力合金涂层的制备及与液态铅铋相容性研究[J]. 材料开发与应用, 2023, 38(6): 9-14.
ZHANG Tianyi, LÜ Shasha, RUAN Zhangshun, FU Xiaogang, LONG Bin, TAO Liu, QIN Bo, LI Zhengcao. Research on Preparation of Stellite Alloy Coating and Its Compatibility with Liquid Lead-Bismuth Eutectic Alloy[J]. Development and Application of Materials, 2023, 38(6): 9-14.
Citation: ZHANG Tianyi, LÜ Shasha, RUAN Zhangshun, FU Xiaogang, LONG Bin, TAO Liu, QIN Bo, LI Zhengcao. Research on Preparation of Stellite Alloy Coating and Its Compatibility with Liquid Lead-Bismuth Eutectic Alloy[J]. Development and Application of Materials, 2023, 38(6): 9-14.

司太力合金涂层的制备及与液态铅铋相容性研究

基金项目: 

国家原子能机构核材料技术创新中心合作项目(ICMW-2022-Y2)

详细信息
    作者简介:

    张天一,工程物理系博士生。

    通讯作者:

    吕沙沙,博士,副教授。E-mail:lvss@bnu.edu.cn
    付晓刚,硕士,高级工程师。E-mail:fuxiaogang09@126.com

    吕沙沙,博士,副教授。E-mail:lvss@bnu.edu.cn
    付晓刚,硕士,高级工程师。E-mail:fuxiaogang09@126.com

  • 中图分类号: TG665

Research on Preparation of Stellite Alloy Coating and Its Compatibility with Liquid Lead-Bismuth Eutectic Alloy

  • 摘要: 铅冷快堆使用具有更高安全性的液态铅铋合金作为冷却剂,是颇具发展前景的先进四代堆型。本研究围绕耐铅铋腐蚀涂层,在奥氏体不锈钢基体上开展司太力合金涂层的制备,分析其组成成分和微观结构。开展涂层的铅铋腐蚀实验,分析其结构完整性、力学性能、表面氧化层及物相组成变化。通过微观结构和力学性能表征,评估司太力合金涂层的耐铅铋腐蚀性能,从而为铅铋快堆的工程应用提供理论支撑和技术支持。

     

  • [1] 赵熹, 陈映雪, 曾献, 等. 一种铅基快堆用高硅不锈钢的热处理工艺优化及铅铋相容性研究[J]. 工程科学学报, 2020, 42(11):1488-1498.
    [2] ZHANG J S. A review of steel corrosion by liquid lead and lead-bismuth[J]. Corrosion Science, 2009, 51(6):1207-1227.
    [3] FERRÉ F G, MAIROV A, IADICICCO D, et al. Corrosion and radiation resistant nanoceramic coatings for lead fast reactors[J]. Corrosion Science, 2017, 124:80-92.
    [4] SHORT M P, BALLINGER R G, HÄNNINEN H E. Corrosion resistance of alloys F91 and Fe-12Cr-2Si in lead-bismuth eutectic up to 715℃[J]. Journal of Nuclear Materials, 2013, 434(1-3):259-281.
    [5] KIESER M, MUSCHER H, WEISENBURGER A, et al. Liquid metal corrosion/erosion investigations of structure materials in lead cooled systems:part 1[J]. Journal of Nuclear Materials, 2009, 392(3):405-412.
    [6] KONDO M, TAKAHASHI M, SUZUKI T, et al. Metallurgical study on erosion and corrosion behaviors of steels exposed to liquid lead-bismuth flow[J]. Journal of Nuclear Materials, 2005, 343(1-3):349-359.
    [7] FETZER R, WEISENBURGER A, JIANU A, et al. Oxide scale formation of modified FeCrAl coatings exposed to liquid lead[J]. Corrosion Science, 2012, 55:213-218.
    [8] ZHANG J S, LI N. Review of the studies on fundamental issues in LBE corrosion[J]. Journal of Nuclear Materials, 2008, 373(1-3):351-377.
    [9] 鞠娜, 雷玉成, 陈钢, 等. 410不锈钢在550℃流动的铅铋共晶合金中的腐蚀行为[J]. 材料导报, 2019, 33(20):3489-3493.
    [10] 王凯琳, 李良星, 张双雷, 等. 轴流铅铋泵的设计及其水力性能分析[J]. 西安交通大学学报, 2020, 54(11):166-174.
    [11] CHARALAMPOPOULOU E, LAMBRINOU K, VAN DER DONCK T, et al. Early stages of dissolution corrosion in 316L and DIN 1.4970 austenitic stainless steels with and without anticorrosion coatings in static liquid lead-bismuth eutectic (LBE) at 500℃[J]. Materials Characterization, 2021, 178:111234.
  • 加载中
计量
  • 文章访问数:  61
  • HTML全文浏览量:  6
  • PDF下载量:  18
  • 被引次数: 0
出版历程
  • 收稿日期:  2023-04-19
  • 网络出版日期:  2024-01-10

目录

    /

    返回文章
    返回